J52-4 Chlorosulfonated Polyethylene Anti-Broken Coating (primer/cover, two component)Product descriptionØ Based on chlorosulfonated polyethylene rubber, adding special resin, filler, plasticizer, solvent etc. For primer and cover, A component
Detailed introduction to J52-4 Chlorosulfonated Polyethylene Anti-Broken Coating (primer/cover, two component):
J52-4 Chlorosulfonated Polyethylene Anti-Broken Coating (primer/cover, two component)
Product description
Ø Based on chlorosulfonated polyethylene rubber, adding special resin, filler, plasticizer, solvent etc. For primer and cover, A component is the paint slurry of primer and cover, B component the universal curing agent of primer and cover paint.
Ø Good anti-broken and resistance for acid, alkali, salt, climate aging, chemical atmosphere, drying fast, low temperature operating.
Recommended uses
As anti-broken surface and anti-corrosive protecting for chemical solution corrosion and water corrosion in building structure.
Physical parameter | |
Color | Primer: translucence or undertone; Cover: all colors |
Glossy | Semi gloss |
Theoretic coverage | Primer: 180g/, cover: 180g/ |
Specific gravity | About 1.18 |
Desiccation time | 23±2: surface dryness≤0.5h, Actual dryness≤24h |
Absolute solidification | 23±2: 7 days |
Flash point | A:10, B:16 |
Storage | A:6 months, B:6 months |
The surface that is smeared must be cleaned drastically before construction. Make sure theres no rustoil stainwater spotdust and etc. Paint the antirust primer after the descaling. In the operation interval, paint the second antirust paint,interim paint; The layer of one time should above 3 layers(film thickness above 80um), than can be installed and paint the following paint. The surface roughness concentration of sand blasting at 40-70um, should add the layer of primer to make sure the effective thickness of the primer. The organic solvent of the paint will volatilize in the process of construction, we should reinforce aeration and exhaust in executive locale. This paint belongs to dangerous goods. It should be lied in the place that is drynessaerationshady and cool, away from heat source, avoided shining directly by sunshine, and it should isolate tinder. Avoid inbreathing solvent steam or paint fog chronically, eyes and shin cannot contact this product, when workers construct in the place that is limited and air is un-current, we must provide the powerful airiness and wear safety appliances. |
Packing specifications |
A component : 17kg; B component : 17kg(according to the quota adding A component in using) |