1.dry quickly
2.excellent physical and mechanical property
3.water resistance, resistance of acid-base corrosion
Detailed introduction to High Chlorinated Polyethylene Anticorrosive Paint:
FXGL-3 High Chlorinated Polyethylene Anticorrosive Finish
(different colors) (use for steel structure)
Operative norm: SH 3022-99
Characteristics: dry quickly, excellent physical and mechanical
property,water resistance,resistance of acid-base corrosion
property, resistance of elements,construction property, it can still
construct in -20°C.
Uses: mainly use for anticorrosion of petrochemical equipment,
pipeline,concrete construction etc. which erode by petrochemical
atmosphere environment. Also use for railway,bridge,high tension
transmission line,offshore drilling and oil production facilities, kinds of vehicle chassis,heavy machinery.
Technical target
Mixing ratio: single component
Standard film thickness: Dry: 30μm/coat
Academic spreading rate: 0.11kg/ m2/30μm
Solid contents: 58%
Humidity requirement: below 85%
Drying time & Coating interval
Temperature°C
Dry to touch min
Dry semi-hard hrs
Min. interval hrs
Max. interval d | -10 0 10 20 30
60 50 40 30 20
12 8 6 5 4
12 8 6 5 4
|
Substrate treatment
Primer or intermediate paint surface should be clean and dry, no
feculence
Matching
Applicable under coatings
High Chlorinated Polyethylene Anticorrosive Intermediate Paint
High Chlorinated Polyethylene Anticorrosive Primers